Some leads on components may have exposed copper, areas where the (tin) plating may not be present. This can sometimes be incorrectly identified as a tarnished or oxidized lead. Regarding solderability and function, please see our product managers response below:
“That will not affect the parts functionality. The parts are fine for use.”
-If there is much larger areas not tinned, this may potentially affect solderability.